大连海事大学学报 >
2016 , Vol. 42 >Issue 2: 124 - 128
DOI: https://doi.org/10.16411/j.cnki.issn1006-7736.2016.02.020
土壤中氯离子对无溶剂环氧石油沥青涂层的腐蚀行为
收稿日期: 2015-10-30
修回日期: 2016-01-11
网络出版日期: 2016-01-11
基金资助
国家自然科学基金资助项目（21276036）；中央高校基本科研业务费专项资金资助项目（3132014323）.
Effect of chlorine ion in soil on corrosion behavior of solvent-free coal asphalt coating
Received date: 2015-10-30
Revised date: 2016-01-11
Online published: 2016-01-11
为考察无溶剂环氧石油沥青涂层在不同氯离子浓度土壤中的腐蚀行为,采用电化学测试技术的方法测试涂层的腐蚀电位和低频阻抗模值.结果表明,随着土壤中氯离子含量的增加,涂层的腐蚀电位负移,容抗弧半径减小,阻抗模值降低,说明土壤中氯离子含量的增加导致涂层对土壤中腐蚀性介质的屏蔽作用能力有所下降.400 μm厚的涂层在29% H2O+1.8% NaCl土壤中的交流阻抗谱图呈现单容抗弧特征,随着埋设时间的延长,阻抗模值下降,埋设360 d时涂层的低频阻抗模值达到8.3020×108 Ω•cm 2,涂层未发生鼓泡、裂缝和剥落迹象.表明涂层形成了有效的屏蔽层,对基体金属有着良好的防护作用.
关键词： 土壤; 氯离子; 无溶剂环氧石油沥青涂层; 腐蚀行为
李瑞超 , 梁成浩 , 黄乃宝 , 等 . 土壤中氯离子对无溶剂环氧石油沥青涂层的腐蚀行为[J]. 大连海事大学学报, 2016 , 42(2) : 124 -128 . DOI: 10.16411/j.cnki.issn1006-7736.2016.02.020
To analyze the corrosion behavior of solvent-free coal asphalt coating in different chloride ion concentration, the corrosion potential and the low frequency impedance modulus of the coating were tested by electrochemical technique. Results show that with the increase of chloride ion content in soil, coating corrosion potential negative shift, capacitive reactance arc radius and the impedance modulus value reduce, which indicates that the increase of chloride ion content in soil will lead to a decrease in the shield ability of the coating to the corrosive medium in soil.The EIS of coating with 400 μm immerses in soil of 29% H2O+1.8% NaCl appears only one capacitive reactance arc. With the extension of time buried, the impedance value decreases, and the resistance is 8.3020×108 Ω•cm2 for 360 days.There is no signs of bubbling, cracking and spalling,which shows that the coating forms the effective shielding layer with a good protective effect on matrix metal.
Key words： soil; chlorine ion; solvent-free epoxy asphalt coating; corrosion behavior
[1]LEGGHE E,ARAGON E,BÉLEC L,et al.Correlation between water diffusion and adhesion loss,study of an epoxy primer on steel[J].Progress in Organic Coatings,2009,66(3):276-280.
[2]张剑飞,李博文,陈玉滨.新型管道重防腐环氧粉末涂料的研制与应用[J].现代涂料与涂层,2013,16(2):22-24.
ZHANG Jian-fei,LI Bo-wen,CHEN Yu-bin.Preparation and application of the new pipeline heavy anticorrosion epoxy powder coatings[J].Modern Paint Finishing,2013,16(2):22-24.(in Chinese)
[3]喻林.管道防腐粉末涂料用环氧树脂的研制[J].涂料技术与文摘,2014,35(12):22-23.
YU Lin.Preparation of epoxy resin for anticorrosive powder coatings for pipeline[J].Coatings Technology & Abstracts,2014,35(12):22-23.(in Chinese)
[4]刘翰锋,郑怀玉,张光,等.双组分喷涂型无溶剂超厚膜环氧重防腐涂料的研制[J].中国涂料,2012,27(11):37-41.
LIU Han-feng,ZHENG Huai-yu,ZHANG Guang,et al.Preparation of two-component spray solvent-free ultra-high build epoxy heavy-duty coatings[J].China Coatings,2012,27(11):37-41.(in Chinese)
[5]李杰,陈群尧,李红旗,等.无溶剂环氧石油沥青防蚀涂层研究[J].腐蚀与防护,1999,20(2):73-74.
LI Jie,CHEN Qun-yao,LI Hong-qi,et al.A research on solvent-free epoxy asphalt heavy duty coating[J].Corrosion & Protection,1999,20(2):73-74.(in Chinese)
[6]OGUZIE E E,AGOCHUKWU I B,ONUCHUKWU A I.Monitoring the corrosion susceptibility of mild steel in varied soil textures by corrosion product count technique[J].Materials Chemistry and Physics,2004, 84(1):1-6.
[7]LOPEZ E,OSELLA A,MARTINO L.Controlled experiments to study corrosion effects due to external varying fields in embedded pipelines[J].Corrosion Science,2006,48(2):389-403.
[8]杨小刚,贾淑香,田边弘往,等.无溶剂超厚膜环氧涂层海洋腐蚀模拟试验研究[J].中国港湾建设,2012,179(2):76-80.
YANG Xiao-gang,JIA Shu-xiang,HIROYUKI T,et al.Experimental study on epoxy solvent-free coating in simulated marine corrosion environment[J].China Harbour Engineering,2012,179(2):76-80.(in Chinese)
[9]岳跃法,方倩,阮景阳,等.无溶剂环氧饮水管路防腐涂料的制备及性能研究[J].中国涂料,2013,28(4):43-46.
YUE Yue-fa,FANG Qian,RUAN Jing-yang,et al.Preparation and properties study of solvent-free epoxy anti-corrosion coatings applied in drinking water pipes[J].China Coatings,2013,28(4):43-46.(in Chinese)
[10]袁晓艳,程原,李婧.无溶剂环氧重防腐涂料的研究[J].现代涂料与涂装,2014,17(4):1-3.
YUAN Xiao-yan,CHENG Yuan,LI Jing.Study on solvent-free epoxy heavy-duty coating[J].Modern Paint & Finishing,2014,17(4):1-3.(in Chinese)
[11]GUILLAUMIN V,LANDOLT D.Effect of dispersion agent on paint on steel studied by scanning acoustic microscopy and the degradation of a water borne impedance[J].Corrosion Science,2002,44(1):179-189.
[12]ZHANG Jin-tao, HU Ji-ming, ZHANG Jian-qing,et al.Studies of impedance models and water tranport behaviors of polypropylene coated matals in NaCl solution[J].Progress in Orgranic Coatings,2004,49(4):293-301.
[13]ZHU Cheng-fei,XIE Rui,XUE Jin-hua,et al.Studies of the impedance of models and water transport behaviors of cathodiclly polarized coating[J].Electrochimica Acta,2011,56(16):5828-5835.
[14]杨海,陆卫中,李京,等.环氧粉末涂层在1.5mol/L NaCl 溶液中的失效行为[J].中国腐蚀与防护报,2014,34(4):382-388.
YANG Hai.LU Wei-zhong,LI Jing,et al.Degradation behavior of fusion bonded epoxy powder coating on Q235 carbon steel in 1.5 mol/L NaCl solution[J].Journal of Chinese Society for Corrosion and Protection,2014,34(4):382-388.(in Chinese)
/
| 〈 |
|
〉 |